Polyamide (Nylon) Series
Polyamide (Nylon) 612
PA612 of SDEP having excellent toughness and chemical resistance is mainly used asMonofilament for tooth brush, Textile,?Cable covering, etc .
|
Test
|
Test Method(ASTM)
|
Unit
|
PA612
|
|
Tensile strength
|
D-638
|
kgf/cm2
|
610
|
|
Elongation
|
D-638
|
%
|
90
|
|
Flexural strength
|
D-790
|
kgf/cm2
|
820
|
|
Flexural modulus
|
D-790
|
kgf/cm2
|
22,100
|
|
Izod impact-notch(3.2t)
|
D-256
|
kgf.cm/cm
|
>4.0
|
|
Izod impact-notch(6.4t)
|
D-256
|
kgf.cm/cm
|
>5.0
|
|
HDT(4.6)
|
D-648
|
℃
|
162
|
|
HDT(18.5)
|
D-648
|
℃
|
69
|
|
Melting Temp.
|
D-2240
|
℃
|
185
|
|
MFI (235℃,2.16kg)
|
D-1238
|
g/10min
|
20
|
|
Rockwell Hardness
|
D-785
|
R scale
|
105
|
|
Density
|
D-792
|
g/m3
|
1.06
|
Polyamide (Nylon) 610
- Compare with the Nylon 6 and the Nylon 66, PA 610 of SDEP is more softer, has low water absorption, better resistance to low temperature and dimensional stability.
- PA 610 has good oil resistance, chemical resistance and electric properties, belongs to the self-extinguishing material.
- Application : Tooth brush's bristle-like monofilament, Monofilament, Cable covering, etc..
|
Test
|
Test Method (ASTM)
|
Unit
|
PA 610
|
|
Tensile strength
|
D-638
|
kgf/cm2
|
> 500
|
|
Elongation
|
D-638
|
%
|
> 100
|
|
Bending Strength
|
|
kgf/cm2
|
> 500
|
|
Melting Temp.
|
D-2240
|
℃
|
208~220
|
|
Density
|
D-792
|
g/m3
|
1.07~1.13
|
Polyamide (Nylon) 12
- PA 12 of SDEP has very good toughness and the lowest water absorption among Polyamides, good dimensional stability, oil resistance and alkali proof, non toxic under low temperature,
- Application : Extrusion, injection molding, blow molding or producing into powder spraying coating
- Meet the DIN 73378, 74324, ISO 7628 SAE J844 regulations.
- Meet the HMS-PS-105(HMC/KMC) Condition
|
Test
|
Test Method (ASTM)
|
Unit
|
PA1212C
|
PA1212C-01
|
|
Tensile strength
|
D-638
|
kgf/cm2
|
>400
|
>470
|
|
Elongation
|
D-638
|
%
|
>280
|
>260
|
|
Flexural strength
|
D-790
|
kgf/cm2
|
>500
|
>130
|
|
Flexural modulus
|
D-790
|
kgf/cm2
|
>12,500
|
>2,800
|
|
Izod impact-notch(3.2t)
|
D-256
|
kgf.cm/cm
|
>7.2
|
NB
|
|
Izod impact-notch(6.4t)
|
D-256
|
kgf.cm/cm
|
>7.7
|
NB
|
|
HDT(4.6)
|
D-648
|
℃
|
109
|
113
|
|
HDT(18.5)
|
D-648
|
℃
|
51
|
55
|
|
Melting Temp.
|
D-2240
|
℃
|
185
|
176
|
|
MFI (235℃,2.16kg)
|
D-1238
|
g/10min
|
10
|
3
|
|
Density
|
|
g/m3
|
1.03
|
1.05
|
Polyamide (Nylon) 12 for Tube
|
Test
|
Test Method (ASTM)
|
Unit
|
Vestamid x7293
|
PA1212C-01
|
|
Tensile strength
|
D-638
|
kgf/cm2
|
270
|
514
|
|
Elongation
|
D-638
|
%
|
|
367
|
|
Flexural strength
|
D-790
|
kgf/cm2
|
|
160
|
|
Flexural modulus
|
D-790
|
kgf/cm2
|
|
3,181
|
|
Izod impact-notch(3.2t)
|
D-256
|
kgf.cm/cm
|
|
NB
|
|
Izod impact-notch(6.4t)
|
D-256
|
kgf.cm/cm
|
|
NB
|
|
HDT(4.6)
|
D-648
|
℃
|
|
113
|
|
HDT(18.5)
|
D-648
|
℃
|
|
55
|
|
Melting Temp.
|
D-2240
|
℃
|
172
|
176.33
|
|
MFI (235℃,2.16kg)
|
D-1238
|
g/10min
|
10
|
2.8
|
|
Water absorption
|
|
%
|
-
|
-
|
|
Density
|
|
g/m3
|
1.02
|
1.05
|
YoureTOP for Instrument Panel
- Excellent dimensional stability
- Good mechanical properties
- Good surface
- UV stability / UV- resistance
InYourSide's material for Instrument Panel
YT CAIW20 PC/ABS alloy, Good surface Heat resistant, GF 50% filled
Properties of?YT CAIW20
- YT CAIW20 is specially designed Polycarbonate and ABS Alloy for Instrument Panel and Center fascia of Automotive.
- Meets MS 214-02(HMC/KMC), EDS-M-4641(GM-DAT) conditions.
|
Items
|
Test Method (ASTM)
|
EDS-M-4641
|
MS Spec214-02
|
Results
|
|
Specific Gravity
|
D-792
|
1.13 ±0.02
|
1.14 ±0.01
|
1.14
|
|
Elongation at break
|
D-638
|
>100
|
>105
|
>110
|
|
Tensile strength
|
D-638
|
>550
|
>530
|
570 kg/cm2
|
|
Flexural strength
|
D-790
|
>750
|
>770
|
800 kg/cm2
|
|
Flexural modulus
|
D-790
|
>22,000
|
>21,000
|
23,000 kg/cm2
|
|
IZOD impact strength (at 20/-40 ℃)
|
D-256
|
N.B/>30
|
>46/>20
|
NB/30 kg*cm/cm
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>110
|
>110
|
128 ℃
|
|
Rockwell Hardness
|
D-785
|
>115
|
>114
|
117 R
|
YoureTOP for Mirror Plate and Housing
- Excellent heat resistance
- Good mechanical properties
- Good surface
- UV stability / UV- resistance
InYourSide's material for Mirror plate and housing
- YTP 7250 / YT60HG50 Conventional PA6, Good surface Heat resistant, GF 50% filled
- YTP 7260 / YT 60HG60 PA6, Good surface, UV-resist. Heat resistant, GF 60% filled
- YTP 8260 / YT 66HG60 PA66, Good surface, UV resist. Heat resistant, GF 60% filled
Properties of YTP 7250 / YT 60HG50
- YTP 7250 / YT 60HG50 is 50% of Glass fiber reinforced Polyamide 6(Nylon 6) specially designed for Outside Mirror base plate.
- Meets MS 211-64(HMC/KMC), EDS-M-5127(GM-DAT) Conditions.
|
Items
|
Test Method (ASTM)
|
EDS-M-5127
|
MS Spec MS 211-64
|
Results
|
|
Specific Gravity
|
D-792
|
1.54 ±0.02
|
1.56 ±0.03
|
1.56
|
|
Tensile strength
|
D-638
|
>2,000
|
>2,000
|
2,200 kg/cm2
|
|
Flexural strength
|
D-790
|
>3,000
|
>2,700
|
3,200 kg/cm2
|
|
Flexural modulus
|
D-790
|
>130,000
|
>135,000
|
135,000 kg/cm2
|
|
IZOD impact strength (at 20℃)
|
D-256
|
>15
|
>9
|
16.0 kg*cm/cm
|
|
IZOD Impact strength (at -30℃)
|
D-256
|
>10
|
>7
|
11.8 kg*cm/cm
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>215
|
>200
|
252 ℃
|
|
Ash Content
|
D-5630
|
50 ± 3
|
50 ± 2
|
50 %
|
Properties of YTP 7260 / YT 60HG60
- YTP 7260 / YT 60HG60 is 60% of Glass fiber reinforced Polyamide 6 (Nylon 6) specially designed for Outside Mirror Base Plate
- Meets MS 211-64(HMC/KMC), EDS-M-5127(GM-DAT) Conditions
|
Items
|
Test Method (ASTM)
|
EDS-M-5127
|
MS Spec MS 211-64
|
Results
|
|
Specific Gravity
|
D-792
|
1.54 ±0.02
|
1.56 ±0.03
|
1.56
|
|
Tensile strength
|
D-638
|
>2,000
|
>2,000
|
2,200 kg/cm2
|
|
Flexural strength
|
D-790
|
>3,000
|
>2,700
|
3,100 kg/cm2
|
|
Flexural modulus
|
D-790
|
>130,000
|
>135,000
|
145,000 kg/cm2
|
|
IZOD impact strength (at 20℃)
|
D-256
|
>15
|
>9
|
16.0 kg*cm/cm
|
|
IZOD Impact strength (at -30℃)
|
D-256
|
>10
|
>7
|
11.8 kg*cm/cm
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>215
|
>200
|
252 ℃
|
|
Ash Content
|
D-5630
|
50 ± 3
|
50 ± 2
|
50 %
|
Properties of YTP 8260 / YT 66HG60
- YTP 8260 / YT 66HG60 is 60% of Glass fiber reinforced Polyamide 66 (Nylon 66) specially designed for Outside Mirror Base Plate and Housing
- Meets MS 211-64(HMC/KMC), EDS-M-5166(GM-DAT) conditions
|
Items
|
Test Method (ASTM)
|
EDS-M-5166
|
MS Spec 211-64
|
Results
|
|
Specific Gravity
|
D-792
|
1.70
|
1.70 ±0.02
|
1.70
|
|
Tensile strength
|
D-638
|
>2,000
|
>1,700
|
2,100 kg/cm2
|
|
Flexural strength
|
D-790
|
>3,000
|
>2,800
|
3,000 kg/cm2
|
|
Flexural modulus
|
D-790
|
>160,000
|
>160,000
|
170,000 kg/cm2
|
|
IZOD impact strength (at 20℃)
|
D-256
|
>15
|
>8
|
16.0 kg*cm/cm
|
|
IZOD Impact strength (at -30℃)
|
D-256
|
>10
|
>7
|
12.0 kg*cm/cm
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>215
|
>208
|
225 ℃
|
|
Rockwell Hardness
|
|
>120
|
-
|
125 R
|
|
Ash Content
|
D-5630
|
60
|
60 ± 2
|
60 %
|
YoureTOP for Radiator tank
- Excellent heat resistance150℃ for long term stability and stiffness athigh temp.
- Resistance to engine oils or chemicals
- Mechanical properties
- CaCl2 resistance
InYourSide's material for Radiator Tank
- YT 66HG30Conventional PA66, Heat resistant, GF 30% filled
- YT 66HG33Conventional PA66, Heat resistant, GF 33% filled
Properties of YT 66HG30
- YT 66HG30 is 30% of Glass fiber reinforced and Heat resistant PA66 designed for Radiator end tank of Automotive.
- Meets MS 211-47 A-2 (HMC/KIA) Condition
|
Items
|
Test Method (ASTM)
|
MS Spec
211-47 Type A-2
|
Results
|
|
Tensile strength
|
D-638
|
>1,600
|
1,900 kg/cm2
|
|
Flexural strength
|
D-790
|
>2,100
|
2,600 kg/cm2
|
|
Flexural modulus
|
D-790
|
>65,000
|
94,000 kg/cm2
|
|
IZOD impact strength
|
D-256
|
>9
|
16.0 kg*cm/cm
|
|
Rockwell hardness
|
D-785
|
>112
|
118 R
|
|
Melting temperature
|
|
>210
|
261 ℃
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>235
|
252 ℃
|
|
Ash Content
|
D-5630
|
33 ± 2
|
30 %
|
Properties of YT 66HG33
- YT 66HG33 is 33% of Glass fiber reinforced and Heat resistantPA66 designed forRadiator end tank of Automotive.
- Meets MS 211-47 A-2 (HMC/KIA) Condition
|
Items
|
Test Method (ASTM)
|
MS Spec
211-47 Type A-2
|
Results
|
|
Tensile strength
|
D-638
|
>1,600
|
1,880 kg/cm2
|
|
Flexural strength
|
D-790
|
>2,100
|
2,700 kg/cm2
|
|
Flexural modulus
|
D-790
|
>65,000
|
95,000 kg/cm2
|
|
IZOD impact strength
|
D-256
|
>9
|
16.0 kg*cm/cm
|
|
Rockwell hardness
|
D-785
|
>112
|
118 R
|
|
Melting temperature
|
|
>210
|
261 ℃
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>235
|
252 ℃
|
|
Ash Content
|
D-5630
|
33 ± 2
|
33 %
|
YoureTOP for Fan / Shroud
- Excellent heat resistance
- Resistance to engine oils or chemicals
- Mechanical properties
- Optimal price-quality balance
- Good surface and Dimensional stability
InYourSide's material for Fan / Shroud
YT 66HD34 MS211-47 Type C registered for both Fan and Shroud. Glass fiber and Mineral filler co-mixed.
Properties of YT 66HD34
- YT 66HGM34 is 38% of Glass fiber and Mineral filler reinforcedand Heat resistant PA66 designed for Cooling Fan / Shroud of Automotive.
- Meets MS 211-47 Type C(HMC/KMC), EDS-M-5171(GM-DAT) conditions.
|
Items
|
Test Method (ASTM)
|
EDS-M-5171
|
MS Spec
211-47
|
Results
|
|
Tensile strength
|
D-638
|
>1,200
|
>1,000
|
1,250 kg/cm2
|
|
Flexural strength
|
D-790
|
>1,700
|
>1,500
|
1,800 kg/cm2
|
|
Flexural modulus
|
D-790
|
>70,000
|
>60,000
|
75,000 kg/cm2
|
|
IZOD impact strength (at 23℃)
|
D-256
|
>5.5
|
>3
|
5.5 kg*cm/cm
|
|
Rockwell hardness
|
D-785
|
>120
|
>113
|
120 R
|
|
Melting temperature
|
|
-
|
250~265
|
260 ℃
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>230
|
>210
|
240 ℃
|
|
Annealing Test, 140℃*1000hrs
|
MS211-47
|
-
|
<25%
|
Under 10%
|
|
Ash Content
|
D-5630
|
40±3
|
35~43
|
38 %
|
YoureTOP for Engine Beauty Cover
- Heat resistance
- Resistance to engine oils or chemicals
- Mechanical properties
- Dimensional Stability
InYourSide's material for Engine Beauty Cover
- YT 66HD25 Designed by MS211-60, PA66, GF/MF 38%, Heat resistance
- YT 60HD12 Designed by MS211-60, PA6, GF/MF 20%, Heat resistance
Properties of YT 66HD25
- YT 66HD25 is 38% of Glass fiber and Mineral Filler reinforced and Heat resistant PA66 specially designed for Engine Beauty Cover of Automotive..
- Meets MS 211-60 Type B Condition
|
Items
|
Test Method (ASTM)
|
MS Spec 211-60
|
Results
|
|
Specific gravity
|
|
1.44~46
|
1.45
|
|
Tensile strength
|
D-638
|
>1,085
|
1,100 kg/cm2
|
|
Flexural strength
|
D-790
|
>1,800
|
1,900 kg/cm2
|
|
Flexural modulus
|
D-790
|
>61,000
|
65,000 kg/cm2
|
|
IZOD impact strength at 23℃
|
D-256
|
>3.8
|
5.0 kg*cm/cm
|
|
IZOD impact strength at -30℃
|
D-256
|
>3.3
|
3.5 kg*cm/cm
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>230
|
240 ℃
|
|
Ash Content
|
D-5630
|
38±2
|
38 %
|
Properties of YT 60HD12
- YT 60HD12 is 20% of Glass fiber and Mineral filler reinforced PA6 desinged for Engine Beauty Cover of Automotive., MF13%
- Meets MS 211-60 Type A-1 Condition
|
Items
|
Test Method (ASTM)
|
MS Spec 211-60
|
Results
|
|
Specific gravity
|
|
1.26~30
|
1.28
|
|
Tensile strength
|
D-638
|
>950
|
980 kg/cm2
|
|
Flexural strength
|
D-790
|
>1,500
|
1,550 kg/cm2
|
|
Flexural modulus
|
D-790
|
>44,000
|
45,000 kg/cm2
|
|
IZOD impact strength at 23℃
|
D-256
|
>3.0
|
4.0 kg*cm/cm
|
|
IZOD impact strength at -30℃
|
D-256
|
>2.5
|
3.5 kg*cm/cm
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>180
|
185 ℃
|
|
Ash Content
|
D-5630
|
20±2
|
20 %
|
YoureTOP for Roof Rack
- Heat resistance
- Weather stability
- Excellent mechanical properties
- Good impact strength
InYourSide's material for Roof Rack
YT 66IW20 Designed by MS211-46 Type C2(HMC/KIA), PA66 Impact reinforced, High weather stability (passed 1200hrs aging test)
Properties of YT 66IW20
- YT 66IW20 is a impact modified, and UV-resistant Polyamide 66 specially designed for Roof Rack of Automotive.
- Meets MS 211-46 Type C-2 (HMC/KIA) Condition.
|
Items
|
Test Method (ASTM)
|
MS Spec
211-46
Type C-2
|
Results
|
|
Specific gravity
|
D-792
|
1.05~.12
|
1.12
|
|
Tensile strength
|
D-638
|
>450
|
495 kg/cm2
|
|
Elongation at break
|
D-638
|
>55
|
63 %
|
|
Flexural strength
|
D-790
|
>600
|
605 kg/cm2
|
|
Flexural modulus
|
D-790
|
>13,000
|
16,540 kg/cm2
|
|
IZOD impact strength at 23℃
|
D-256
|
>70
|
No Break
|
|
IZOD impact strength at -30℃
|
D-256
|
>15
|
15.1 kg*cm/cm
|
|
Heat Deflection Temperature, 18.6kg
|
D-648
|
>60
|
65 ℃
|
YoureTOP for Fastner
- Fast Cycle Time
- High Release
- Good surface
- Excellent Mechanical Properties
InYourSide's material for Fastner
A205F Rhodia's High Release Grade UL 94 V-2, Natural and Black Color.
YoureTOP for Monofilament
- Fast Cycle Time
- High Release
- Good surface
- Excellent Mechanical Properties
InYourSide's material for Monofilament
31A Rhodia's High Viscosity Grade UL 94 V-2, Natural and Black Color.
|